\(k_1\) | \(1.77 \cdot 10^{-5}\) s\(^{-1}\) |
\(k_2\) | \(9.30 \cdot 10^{2}\) s\(^{-1}\) |
\(E_1/R\) | 9, 200 K |
\(E_2/R\) | 6, 450 K |
n | 0.91 |
m | 0.37 |
\(\Delta H\) | 570 J/g |
\(\eta _0\) | \(3.10\cdot 10^{-12}\) Pa s |
B | 10800 K |
C | 27 |
d | 1.77 |
\(c_\parallel \) | \( 9.43\cdot 10^{-13}\) m\(^2\) |
\(c_\perp \) | \(2.50\cdot 10^{-12}\) m\(^2\) |
\(V_{fa}\) | \(78.5\%\) |
\(p_0\) | 0.1203 J/gK |
\(p_1\) | 0.005 J/gK\(^2\) |
\(q_0\) | 0.5905 J/gK |
\(q_1\) | 0.0019 J/gK\(^2\) |
\(\rho _\text {resin}\) | 1.26 g/cm\(^3\) |
\(\rho _\text {fiber}\) | 1.80 g/cm\(^3\) |
\(V_{f0}\) | \(57\% \) |
\(\lambda _{11}\) | 5.80 W/mK |
\(\lambda _{22}\) | 0.57 W/mK |
\(\lambda _{33}\) | 0.57 W/mK |